The impact of sodium periodate oxidation and alginate coating on the capillarity of jute fabric
Ivanovska, Aleksandra; Milosevic, Marija; Ladarevic, Jelena; Tarbuk, Anita; Svircev, Zorica; Kostic, Mirjana
通讯作者Ivanovska, A
来源期刊JOURNAL OF ENGINEERED FIBERS AND FABRICS
ISSN1558-9250
出版年2024
卷号19
英文摘要This study explores the impact of sodium periodate oxidation time (30 min, 60 min, or 120 min) and alginate coating on the capillarity of jute fabrics. Raw jute fabric exhibits a rapid increase in capillary rise height (h) over time, reaching 72 mm at 1200 s. Fabrics oxidized for 30, 60, and 120 min show significantly lower h values of 19, 18, and 28 mm at 1200 s, respectively, which can be ascribed to the oxidation process itself. Precisely, oxidation-induced conversion of hydroxyl groups of cellulose (the main constituent of jute fiber) to aldehyde groups contributed to the fabric reduced affinity for water, hence negatively affecting its capillarity. Approximately 47% and 55% lower h values of fabrics oxidized for 30 and 60 min compared to that oxidized for 120 min can be explained by their lower weight loss after oxidation as well as less pronounced liberation of elementary fibers. Oxidized fabrics characterized by low capillarity can be used for the manufacturing of packaging materials, outdoor gear, and protective covers for crops. To expand jute fabric applications in biocarpet engineering, that is, to obtain polysaccharide-based supports, raw and oxidized jute fabrics were treated with a 1% sodium alginate solution. At 1200 s, oxidized fabrics coated with alginate exhibited 4.3-5.8 times higher h values compared to solely oxidized counterparts. The diffusion coefficients of oxidized fabrics coated with alginate increase up to 35% with prolonged oxidation, emphasizing the oxidation impact on alginate binding.
英文关键词Jute oxidation sodium periodate capillarity diffusion coefficient
类型Article
语种英语
开放获取类型gold
收录类别SCI-E
WOS记录号WOS:001198681700001
WOS关键词DESERTIFICATION ; HEMICELLULOSES ; SORPTION ; CRUSTS
WOS类目Materials Science, Textiles
WOS研究方向Materials Science
资源类型期刊论文
条目标识符http://119.78.100.177/qdio/handle/2XILL650/404435
推荐引用方式
GB/T 7714
Ivanovska, Aleksandra,Milosevic, Marija,Ladarevic, Jelena,et al. The impact of sodium periodate oxidation and alginate coating on the capillarity of jute fabric[J],2024,19.
APA Ivanovska, Aleksandra,Milosevic, Marija,Ladarevic, Jelena,Tarbuk, Anita,Svircev, Zorica,&Kostic, Mirjana.(2024).The impact of sodium periodate oxidation and alginate coating on the capillarity of jute fabric.JOURNAL OF ENGINEERED FIBERS AND FABRICS,19.
MLA Ivanovska, Aleksandra,et al."The impact of sodium periodate oxidation and alginate coating on the capillarity of jute fabric".JOURNAL OF ENGINEERED FIBERS AND FABRICS 19(2024).
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Ivanovska, Aleksandra]的文章
[Milosevic, Marija]的文章
[Ladarevic, Jelena]的文章
百度学术
百度学术中相似的文章
[Ivanovska, Aleksandra]的文章
[Milosevic, Marija]的文章
[Ladarevic, Jelena]的文章
必应学术
必应学术中相似的文章
[Ivanovska, Aleksandra]的文章
[Milosevic, Marija]的文章
[Ladarevic, Jelena]的文章
相关权益政策
暂无数据
收藏/分享

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。