	生态友好型固沙材料制备工艺研究
其他题名	Study on Preparation Process of Eco-friendly Sand-fixing Material
	姜雄; 铁生年
来源期刊	硅酸盐通报
ISSN	1001-1625
出版年	2014
卷号	33 期号:9 页码:2402-2408
中文摘要	为有效控制土地沙漠化,改善沙漠地区自然环境,该文以石膏为主要原材料,以沙粒、保水剂、木屑、十二烷基硫酸钠等为辅助材料,制备了一种生态友好型固沙材料。结果表明:在沙粒掺量为30%、保水剂掺量为4%、木屑掺量为8%、十二烷基硫酸钠掺量为0.3%时,该材料性能最佳,此条件下固沙材料抗压强度为3.40 MPa,吸水率为42.33%,保水率为79.37%,孔隙率为44.73%。该材料制备方法简单,成本低,对环境无污染,具有良好的固沙能力,还可以与生物固沙相结合,在沙漠治理方面具有广阔应用前景。
英文摘要	Desertification is one of the most serious ecological environment problems in China. To effectively control desertification and improve the natural environment in desert areas an eco-friendly sand-fixing material was prepared with gypsum as main material,adding suitable amount of sand,water retention agent, sawdust, SDS, et al. The results show that: The obtained best performance with strength is 3. 40 MPa, water absorption is 42. 33%, water retention is 79. 24% and porosity is 44. 73%,under the sand content of 30%,water-retaining agent dosage of 4%, sawdust content of 8%,and SDS content of 0.3%. The sand-fixing material had no pollution to the environment and suitable for plant growth, therefore, it will have a wide application prospect in the desert governance.
中文关键词	生态友好型 ; 石膏基固沙材料 ; 保水性 ; 强度
英文关键词	eco-friendly gypsum based sand-fixing material water-retention capacity strength
语种	中文
国家	中国
收录类别	CSCD
WOS类目	ENVIRONMENTAL SCIENCES
WOS研究方向	Environmental Sciences & Ecology
CSCD记录号	CSCD:5256004
资源类型	期刊论文
条目标识符	http://119.78.100.177/qdio/handle/2XILL650/231322
作者单位	青海大学新能源光伏产业研究中心, 西宁, 青海 810016, 中国
推荐引用方式 GB/T 7714	姜雄,铁生年. 生态友好型固沙材料制备工艺研究[J],2014,33(9):2402-2408.
APA	姜雄,&铁生年.(2014).生态友好型固沙材料制备工艺研究.硅酸盐通报,33(9),2402-2408.
MLA	姜雄,et al."生态友好型固沙材料制备工艺研究".硅酸盐通报 33.9(2014):2402-2408.