	有机涂层在模拟沙漠大气环境下的加速试验研究
其他题名	Study on Accelerated Test of Organic Coating in Desert Atmospheric Environment
	刘金和; 张雅琴; 刘慕懿; 胡喜艳; 雍兴跃
来源期刊	表面技术
ISSN	1001-3660
出版年	2014
卷号	43 期号:4 页码:64-67,96
中文摘要	目的：在较短的时间内获得有机涂层在沙漠大气环境下的腐蚀失效规律。方法针对有机涂层中应用比较广泛的丙烯酸聚氨酯涂层，采用紫外暴晒与吹沙试验相结合的加速试验环境谱进行实验室模拟沙漠大气环境加速老化试验，通过分析涂层质量、厚度、光泽度、表面形貌及电化学阻抗的变化，研究有机涂层的老化失效过程。结果随着加速试验周期的延长，丙烯酸聚氨酯涂层发生了一系列变化，表现为涂层质量减小，厚度减薄，光泽度降低，表面微观缺陷增多，电化学低频阻抗模值减小，防护性能下降。结论通过加速试验，可以快速获得有机涂层在沙漠大气环境下的老化失效规律。
英文摘要	Objective To get the law of failure of the organic coating in the desert atmospheric environment in a relatively short period of time. Methods Acrylic polyurethane coating which is widely used in organic coatings was selected in the test, the accelerated aging test of the organic coating in desert atmospheric environment was carried out using the method of UV exposure and blowing sands test in the laboratory, and the aging process of the organic coating was characterized by changes in coating mass, thickness, gloss, the surface morphology and the electrochemical impedance. Results It turned out that the organic coating began to degrade with the decrease of mass, gloss, thickness and impedance but the increase of micro defects which implied the decrease of coating protective properties with time. Conclusion The law of degradation of the organic coating in desert atmospheric environment could be quickly obtained by accelerated test.
中文关键词	有机涂层 ; 加速试验 ; 沙漠大气环境 ; 防护性能
英文关键词	organic coating accelerated test desert atmospheric environment protective properties
语种	中文
国家	中国
收录类别	CSCD
WOS类目	METALLURGY METALLURGICAL ENGINEERING
WOS研究方向	Metallurgy & Metallurgical Engineering
CSCD记录号	CSCD:5212351
资源类型	期刊论文
条目标识符	http://119.78.100.177/qdio/handle/2XILL650/230792
作者单位	北京化工大学, 有机无机复合材料国家重点实验室, 北京 100029, 中国
推荐引用方式 GB/T 7714	刘金和,张雅琴,刘慕懿,等. 有机涂层在模拟沙漠大气环境下的加速试验研究[J],2014,43(4):64-67,96.
APA	刘金和,张雅琴,刘慕懿,胡喜艳,&雍兴跃.(2014).有机涂层在模拟沙漠大气环境下的加速试验研究.表面技术,43(4),64-67,96.
MLA	刘金和,et al."有机涂层在模拟沙漠大气环境下的加速试验研究".表面技术 43.4(2014):64-67,96.