	无铅易切削镁黄铜的组织与性能
其他题名	Microstructure and Properties of Cutting Lead-free Brass Containing Magnesium
	黄劲松 1; 彭超群 1; 章四琪 2; 黄伯云 1; 马长松 2
ISSN	1673-2812
出版年	2006
卷号	24 期号:6 页码:854-857,886
中文摘要	采用熔铸、挤压、拉拔的方法生产出了以镁代铅的环保型易切削黄铜材.对易切削黄铜的微观组织进行了观察,并对其力学、化学和切削性能分别进行了研究.结果表明:镁黄铜晶内和晶间有白色和黑色的球状第二相粒子分布,该粒子为金属间化合物,具有脆而不硬的特点,对提高合金切削性能有利.半硬态镁黄铜的抗拉强度为550 MPa,屈服强度为280 MPa,延伸率为16.30%,断面收缩率为32.4%.从切削过程中切削力的大小以及切屑的形貌、大小可以判断,镁黄铜的切削性能接近于C3604铅黄铜.镁黄铜在酸中和盐中的耐蚀性均较好,比较而言耐盐性要好一些.
英文摘要	A new environmental friendly cutting brass containing magnesium instead of lead was produced by casting, extruding and drawing. Its microstriictiire was observed arid its mechanical, chemical and cutting properties were stutied. The results show that the global secondary particles which are intennetallics acul are of briuleness and softness distribute in grains and on grainboundries, which is helpful for cutting. The tensile strength, yield strength, elongation and variation of area of halfhard brass containing magnesium are 550 MPa, 280 MPa, 16.30% , 32.4% respectively. The cutting property of brass containing magnesium corresponds to that of brass containing lead C3604 by the size and appearance of chips and the cutting force. The brass containing magnesium has excellent corrosion resistance.
中文关键词	无铅 ; 易切削 ; 黄铜 ; 组织 ; 性能
英文关键词	lead-free cutting brass microstruture property
语种	中文
国家	中国
收录类别	CSCD
WOS类目	ENGINEERING INDUSTRIAL
WOS研究方向	Engineering
CSCD记录号	CSCD:2630759
资源类型	期刊论文
条目标识符	http://119.78.100.177/qdio/handle/2XILL650/219454
作者单位	1.中南大学, 粉末冶金国家重点实验室, 长沙, 湖南 410083, 中国; 2.中南大学,材料科学与工程学院, 长沙, 湖南 410083, 中国
推荐引用方式 GB/T 7714	黄劲松,彭超群,章四琪,等. 无铅易切削镁黄铜的组织与性能[J],2006,24(6):854-857,886.
APA	黄劲松,彭超群,章四琪,黄伯云,&马长松.(2006).无铅易切削镁黄铜的组织与性能.,24(6),854-857,886.
MLA	黄劲松,et al."无铅易切削镁黄铜的组织与性能".24.6(2006):854-857,886.