	稀土对低碳钢耐大气腐蚀性能影响的研究
其他题名	Study of the Effect of Rare Earths on Corrosion Resistance of Mild Steels
	李春艳 1; 王向东 1; 江社明 1; 陈小平 1; 翁宇 2; 张静波 2; 张代明 3
来源期刊	稀土
ISSN	1004-0277
出版年	2005
卷号	26 期号:6 页码:23-28
中文摘要	通过电化学试验和试验室加速腐蚀试验，研究了稀土对低碳钢耐大气腐蚀性能的影响。结果表明：在低碳钢中，仅添加稀土也能明显的提高其耐大气腐蚀性能。运用扫描电镜、X射线衍射仪和273AM398型电化学测量系统等测量分析手段，对稀土在低碳钢中的耐蚀机理进行了研究和探讨得出，稀土通过夹杂物改性，从而减小微区域腐蚀，并促进稳定的保护性腐蚀产物alphaFeOOH的形成，使得锈层更致密，提高了钢的耐大气腐蚀性。
英文摘要	The effect of RE on corrosion resistance of mild steels has been investigated through electrochemical test and indoor accelerating corrosion test. The research results show that the only addition of RE in mild steel could remarkably improve atmospheric corrosion resistance of mild steels, too. The mechanism of RE effect on corrosion resistance of mild steels was studied and discussed through the measuring and analyzing means such as SEM ,XRD and 273A-M398 electrochemical test system. The results show that RE reduced micro-region corrosion of inclusions arid promoted the formation of the steady protective corrosion product-alpha-FeOOH that resulted in the more compact rust layer because RE modified the types and the morphologies of inclusions. So RE improved atmospheric corrosion resistance of mild steel.
中文关键词	稀土 ; 低碳钢 ; 耐蚀性
英文关键词	rare earth mild steel corrosion resistance
语种	中文
国家	中国
收录类别	CSCD
WOS类目	METALLURGY METALLURGICAL ENGINEERING
WOS研究方向	Metallurgy & Metallurgical Engineering
CSCD记录号	CSCD:2176801
资源类型	期刊论文
条目标识符	http://119.78.100.177/qdio/handle/2XILL650/206793
作者单位	1.钢铁研究总院结构材料研究所, 北京 100081, 中国; 2.本溪钢铁公司技术中心, 本溪, 辽宁 117000, 中国; 3.昆明理工大学材料与冶金工程学院, 昆明, 云南 650093, 中国
推荐引用方式 GB/T 7714	李春艳,王向东,江社明,等. 稀土对低碳钢耐大气腐蚀性能影响的研究[J],2005,26(6):23-28.
APA	李春艳.,王向东.,江社明.,陈小平.,翁宇.,...&张代明.(2005).稀土对低碳钢耐大气腐蚀性能影响的研究.稀土,26(6),23-28.
MLA	李春艳,et al."稀土对低碳钢耐大气腐蚀性能影响的研究".稀土 26.6(2005):23-28.